I would use a MIG welder, I don't see any reason to use shielded gas. A mild steel wire will work fine, but I suggest you preheat the area you are going to weld on the barels. If you are talking deep pits, I would hit it, then leave, hit it again, leave, until it is above the barrels lines. Then you should have enough to file and blend in.

David