OB,
You've, no doubt, been around here long enough to have read some of the threads regarding the mechanism that causes the lead/tin solder to deteriorate. I don't fully recall it, but I do recall that it was implied that the mechanism does continue long after any salts are removed from the surface. What a gunsmith "got away with" or didn't hear back on, may sometimes be misleading to him.