I am referring to mild low carbon steel, you have many more options with modern steels. When you subject mild steel that has had the CCH process done to it to temps. above 400 degrees or so you draw or temper it making it less hard. The critical temp. must be reached to impart hardness but the colors can be obtained at lower temps. If your tests yield something else I will be VERY surprised.