Please by all means, educate me. My premise is that the ejectors were shipped out too soft. My guess is they actually used some type of tool steel and over tempered the parts creating something that was not as hard as it should have been. It could indeed be low carbon steel but I thought Grulla was a better maker than that, could be my mistake. Help me out, your the expert. What exactly is the reasons the ejectors are not properly heat treated? If you are able to tell me the alloy that was used to make the part I can properly heat treat them myself. Not looking for an argument but I have run into many heat treating issues with Spanish guns over the years and them having soft parts is no myth.
Steve, your a Gunsmith, as such, you don't know squat!!
The Master has spoken, so it's no use. Your years of experience is all for nought when it comes to Spanish guns.....you fool!
Good Luck!