Quote:
If the correct quench process is used and braced correctly ,they will not warp !!!!!!!!!!!!

Having worked in machine shops for over 35 years & seeing many many parts go from heat treat ovens, vats etc & into quench tanks, by certified & qualified heat treaters I find this statement to be an absolute Absurdity.
It is an absolute impossibility to say that a part raised to its critical temperature & then give a sudden quench that it "WILL NOT WARP".
"IF" it is not raised to that critical temp & given that sudden quench then it will not come out hard but will rather be essentially annealed.

Miller/TN
I Didn't Say Everything I Said, Yogi Berra