If that is the scenario, the Energy Dispersive X-ray (EDX) scanning photomicrograph of the fracture edge would look something like this: from left to right low cycle ductile fatigue "waves in the sand" or "beach marks", then plastic deformation (stretching) "fish eyes", and then terminal cleavage



If an extreme pressure over-load burst there would be no "waves in the sand"