Do you mean sections of turn-of-the-century barrels that did not burst? A valid criticism.
METL has been pretty excited about this and the previous pattern welded barrel study because there are very few images thereof in the metallurgical literature, and almost none of pattern welded barrels.
BTW and relevant. There are images of hull steel plate recovered from the Titanic. The “acid-lined open hearth” hull plate steel, from the works of David Colville & Co., was non-standard AISI 1020, with a slightly higher phosphorus, much higher sulfur, and lower manganese concentration. The tensile strength was 65,000 psi, and the low Mn:S ratio (6.8:1) made the metal more brittle in the cold temperature.
The photomicrographs showed “dirty steel” with both silicate, sulfide, and manganese sulfide inclusions.
This is from "There's Danger in Damascus" by Major J.W. Houlden, June 1950 "C-I-L Oval", a publication of Canadian Industries Limited and reprinted in the 1960 "Guns Digest". Obviously pre-SEM & EDX and of much lower resolution
Burrard published a few photomicrographs also